Extrusion - Pressure Pipe
- XRC20B
- XS10B
Technical Datasheet
Material: HDPE
Grade: XRC20B
Application: Gas, portable water, sewage, industrial pipe, non-conventional pipe installation
Description
HDPE XRC20B is a very high performance hexene-based black compound, with a MRS 10MPa – PE100 classification, particularly appropriate for pressure pipes that are either installed or operated under extreme conditions.
Characteristics
▶ extreme high resistance to crack initiation and to slow crack growth
▶ meeting the highest prescription and standards for PE pipe
▶ easy processing and safe welding properties
| Properties | Test Method | Unit | Value |
| Melt Index (190℃/5kg) | ISO 1133 | g/10min | 0.3 |
| Density | ISO 1183 | g/cm3 | 0.958 |
| Oxygen Induction Time (200℃) | ISO 11357-6 | min | >20 |
| Carbon Black Content | ISO 6964 | % | 2.0~2.5 |
| Carbon Black Dispersion | ISO 18553 | rating | ≤3 |
| Water Content | ISO 15512 | ppm | ≤300 |
| Melting Temperature | Hanwha Total | - | 129 |
| Tensile Strength at Yield | ISO 527 | MPa | 26 |
| Tensile Strength at Break | ISO 527 | MPa | 35 |
| Elongation at Break | ISO 527 | % | ≥700 |
| Flexural Modulus | ISO 178 | MPa | 1,100 |
Technical Datasheet
Material: HDPE
Grade: XS10B
Application: Gas, portable water, sewage, industrial pipe
| Properties | Test Method | Unit | Value |
| Melt Index (190℃/5kg) | ISO 1133 | g/10min | 0.3 |
| Density | ISO 1183 | g/cm3 | 0.959 |
| Oxygen Induction Time (200℃) | ISO 11357-6 | min | >20 |
| Carbon Black Content | ISO 6964 | % | 2.0~2.5 |
| Carbon Black Dispersion | ISO 18553 | rating | ≤3 |
| Water Content | ISO 15512 | ppm | ≤300 |
| Melting Temperature | Hanwha Total | - | 129 |
| Tensile Strength at Yield | ISO 527 | MPa | 26 |
| Tensile Strength at Break | ISO 527 | MPa | 35 |
| Elongation at Break | ISO 527 | % | ≥700 |
| Flexural Modulus | ISO 178 | MPa | 1,100 |